Influence of temperature and applied potential on the permeability of polyphenol films prepared on vitreous carbon in acid and alkaline media

Belhadj Tahar, Noureddine and Savall, André Influence of temperature and applied potential on the permeability of polyphenol films prepared on vitreous carbon in acid and alkaline media. (2013) Journal of Applied Electrochemistry, 43 (6). 595-604. ISSN 0021-891X

(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader

Official URL: http://dx.doi.org/10.1007/s10800-013-0540-7


The electrochemical polymerization of phenol is known to rapidly produce a thin insulating film at the anode surface. This film generally blocks further polymerization. The objective of this study is to show that, depending on the operating conditions, polymeric films resulting from phenol oxidation present different properties and that certain films can be so porous that they allow the oxidation of phenol to continue. The deposition of polyphenol films with improved permeability could be attractive in the removal of phenol from polluted solutions. Polyphenol films were prepared in aqueous solution on a vitreous carbon anode either by cyclic voltammetry or by electro-oxidation at constant potential. The apparent permeability P (%) of the films prepared by these techniques was evaluated by monitoring changes in the electrode response towards phenol and potassium ferricyanide at 25 and 85°C and as a function of the potential applied during electropolymerization performed either in acidic (1 mol L-¹H₂SO₄) or in alkaline (1 mol L-¹ NaOH) aqueous solution. It was shown that: (1) the polyphenol film electrosynthesized in alkaline medium was more permeable than that prepared in acidic medium, (2) the apparent permeability was higher when the polyphenol film was electrosynthesized with simultaneous oxygen evolution and (3) the use of a high temperature in the polyphenol film preparation, especially in the presence of a concomitant oxygen evolution, significantly enhanced its apparent permeability (P ≥ 100 %). These results are interpreted in terms of a mixed-transport mechanism involving both pore and membrane diffusion. The effect of the permeability of the polymeric film on the removal of phenol from aqueous solution by electropolymerization is discussed.

Item Type:Article
Additional Information:Thanks to Springer editor. The original PDF can be found at Journal of Applied Electrochemistry website: http://link.springer.com/article/10.1007%2Fs10800-013-0540-7
HAL Id:hal-02354573
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
Other partners > Université de Monastir - UM (TUNISIA)
Laboratory name:
Deposited On:24 Oct 2013 08:10

Repository Staff Only: item control page