Effect of reinforcing submicron SiC particles on the wear of electrolytic NiP coatings Part 2: Bi-directional sliding.
(2006)
Surface and Coatings Technology, 2 (3-4). 581-589. ISSN 0257-8972
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 810kB |
Official URL: http://dx.doi.org/10.1016/j.surfcoat.2005.12.015
Abstract
As-plated and heat-treated electrodeposited NiP and composite NiP-SiC coatings were investigated in bi-directional ball-on-disc sliding tests. All tests were performed under gross slip conditions. Heat treatment decreases the wear volume loss during fretting in ambient air for all coatings investigated. Heat-treated NiP coating has a lower wear volume loss compared to composite NiP-SiC coatings for all sliding tests. The wear rate at the bi-directional sliding test was found to be lower relative to the wear rate at uni-directional sliding test.
| Item Type: | Article |
|---|---|
| Additional Information: | This publication is available on http://www.sciencedirect.com/science/journal/02578972 |
| HAL Id: | hal-03598144 |
| Audience (journal): | International peer-reviewed journal |
| Audience (conference): | International conference proceedings |
| Uncontrolled Keywords: | |
| Institution: | Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Other partners > Katholieke Universiteit Leuven - KU LEUVEN (BELGIUM) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) Other partners > Russian academy of sciences (RUSSIA) French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) |
| Laboratory name: | |
| Statistics: | download |
| Deposited On: | 04 Sep 2008 11:19 |
Repository Staff Only: item control page