Identification of intermetallic precipitates formed during re-solidification of brazed aluminium alloys.
(2006)
Scripta Materialia, 5 (2). 191-194. ISSN 1359-6462
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 193kB |
Official URL: http://dx.doi.org/10.1016/j.scriptamat.2006.03.038
Abstract
This study shows that Fe and Mn bearing phases in Al–Si alloys containing a low level of Fe and Mn are essentially cubic greek small letter alpha-Al(Fe, Mn)Si with Im3 space group and δ-AlFeSi which is observed with both tetragonal and orthorhombic structures. As this latter phase is not expected to form according to the ternary Al–Fe–Si phase diagram, the present results suggest that it is stabilized in the quaternary Al–Fe–Mn–Si system with respect to other phases such as β-Al4FeSi.
| Item Type: | Article |
|---|---|
| Additional Information: | Thanks to Elsevier editor. The definitive version is available at http://www.sciencedirect.com The original PDF of the article can be found at Scripta Materiala website : http://www.sciencedirect.com/science/journal/13596462 |
| HAL Id: | hal-03599355 |
| Audience (journal): | International peer-reviewed journal |
| Uncontrolled Keywords: | |
| Institution: | Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) |
| Laboratory name: | |
| Statistics: | download |
| Deposited On: | 04 Sep 2008 14:08 |
Repository Staff Only: item control page