Microwave dielectric properties of the spinel composition Mg1+xTixAl2-2xO4

Badev, Alex and Iliev, I. and Cambronne, Jean-Pascal and Lebey, Thierry and Barnabé, Antoine and Levcheva, Valda Microwave dielectric properties of the spinel composition Mg1+xTixAl2-2xO4. (2007) Journal of OptoElectronics and Advanced Materials, 1 (10). 507-509. ISSN 1454-4164

(Document in English)

PDF (Author's version ) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader


The objects of our research is magnesium aluminates (spinel), in which the electric charge of Al3+ cation is partially substituted with constitutive trivalent cation of Mg2+ and Ti 4+ in the system with the following composition: Mg1+xTixAl2-2xO4 with (x) varying from 0,1 to 0,6. X-ray diffraction data shows that within the above values of (x) the composition is a single phase spinel. The microwave basic parameters were measured as εr, tan δ and τf, respectively with the following values: εr = 6-12, tanδ = (1.5-3.5) x 10-4 at 10 GHz and Qf = 70 000 – 90 000, and τf from -50 to -70 ppm/deg.

Item Type:Article
Additional Information:Thanks to National Institute for Research and Development of Optoelectronics editor. The definitive version is available at http://inoe.inoe.ro/Journal.html The original PDF of the article can be found at Journal of OptoElectronics and Advanced Materials website : http://inoe.inoe.ro/Journal.html
HAL Id:hal-03477936
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
Other partners > Sofia University St. Kliment Ohridski (BULGARIA)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Other partners > University of Chemical Technology and Metallurgy of Sophia (BULGARIA)
Laboratory name:
Deposited On:16 Oct 2009 08:16

Repository Staff Only: item control page