Effect of High-Temperature Exposure on Degradation of La0.6Sr0.4CoO3 Coated Metallic Interconnects for ITSOFC and SOEC

Korb, Matias de Angelis and Tarragó, Diego Pereira and Krischer, Cesar Augusto and Duluard, Sandrine Nathalie and Ansart, Florence and Malfatti, Célia de Fraga Effect of High-Temperature Exposure on Degradation of La0.6Sr0.4CoO3 Coated Metallic Interconnects for ITSOFC and SOEC. (2020) Materials Research, 23 (3). 1-7. ISSN 1516-1439

(Document in English)

PDF (Publisher's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader

Official URL: https://doi.org/10.1590/1980-5373-MR-2020-0084


Previous studies showed the formation of new phases affecting the electrical properties of LSC thin films deposited on stainless steel substrates, which are commonly tested for ITSOFC and SOEC interconnects. A 4.3 μm thick La0.6Sr0.4CoO3 coating was deposited on AISI430 steel by spray pyrolysis, followed by heat treatment (800°C/2h) and an oxidation in air (800°C/96h). The La0.6Sr0.4CoO3 phase interacted with the metallic substrate and formed SrCrO4, causing degradation of the perovskite into La0.9Sr0.1CoO3. An EDS mapping showed Sr and Cr enrichment in the coating/substrate interface. TG analysis indicated a lower mass gain for the coated substrate. The total ASR at 800°C of the interconnect before and after oxidation was 3.23 Ω.cm2 and 3.98 Ω.cm2, respectively. The Ea underwent very small variation, remaining around 0.24 eV (T≤300°C) and 0.65 eV (T≥400°C). The reaction of Cr from the substrate and Sr from LSC seems to have impaired the performance of the interconnect.

Item Type:Article
Additional Information:This is an Open Access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
HAL Id:hal-03170651
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Other partners > Instituto Federal Sul-rio-grandense - IFSul (BRAZIL)
Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
Other partners > Universidade Federal do Rio Grande do Sul - UFRGS (BRAZIL)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
Laboratory name:
Deposited On:16 Mar 2021 11:59

Repository Staff Only: item control page