High temperature micromechanical behavior of a Pt-modified nickel aluminide bond-coating and of its interdiffusion zone with the superalloy substrate.
(2020)
Metallurgical and Materials Transactions A, 51 (4). 1475-1480. ISSN 1073-5623
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 424kB |
Official URL: https://doi.org/10.1007/s11661-020-05634-2
Abstract
The micromechanical properties of a b-(Ni,Pt)Al bondcoating was investigated between 700°C and 1000°C using ultrathin freestanding bond-coating specimens. Its brittle-to-ductile transition temperature was close to 750°C, with a significant ductility above 800°C (up to 23 pct at 1000°C). The tensile strength decreased from 450 MPa at 750°C down to 50 MPa at 1000°C. Fractographic observations evidenced the material brittleness at intermediate temperature with large cleaved grains and its ductility above 750°C with important necking of individual grains.
| Item Type: | Article |
|---|---|
| Audience (journal): | International peer-reviewed journal |
| Uncontrolled Keywords: | |
| Institution: | French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) Université de Toulouse > Ecole nationale supérieure des Mines d'Albi-Carmaux - IMT Mines Albi (FRANCE) Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Université de Toulouse > Institut National des Sciences Appliquées de Toulouse - INSA (FRANCE) Université de Toulouse > Institut Supérieur de l'Aéronautique et de l'Espace - ISAE-SUPAERO (FRANCE) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) Other partners > SAFRAN (FRANCE) |
| Laboratory name: | |
| Statistics: | download |
| Deposited On: | 02 Dec 2020 16:32 |
Repository Staff Only: item control page