Verdalet-Guardiola, Xavier
and Saillard, Romain and Fori, Benoit and Duluard, Sandrine and Blanc, Christine
Comparative analysis of the anticorrosive properties of trivalent chromium conversion coatings formed on 2024-T3 and 2024-T351 aluminium alloys.
(2020)
Corrosion Science, 167. 108508. ISSN 0010-938X
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 3MB |
Official URL: https://doi.org/10.1016/J.CORSCI.2020.108508
Abstract
The anticorrosive properties of the trivalent chromium process (TCP) coatings were studied for a 2024 aluminium alloy (AA2024) in both T3 and T351 metallurgical states. Better corrosion resistance was measured for the TCP coated AA2024-T3 compared to AA2024-T351, which was clearly related to the surface copper coverage measured after the pre-treatments for the different samples. The differences were explained considering the reactivity of both the S-phase coarse intermetallics (IMCs) and intergranular Cu-rich precipitates during deoxidation.Large S-phase IMCs and numerous intergranular Cu-rich precipitates constituted critical metallurgical parameters for the anticorrosive properties of the TCP coatings
| Item Type: | Article |
|---|---|
| HAL Id: | hal-03165264 |
| Audience (journal): | International peer-reviewed journal |
| Uncontrolled Keywords: | |
| Institution: | French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Other partners > MECAPROTEC Industries (FRANCE) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) |
| Laboratory name: | |
| Funders: | French Ministry of Economy and industry (BPI-France), the Région Occitanie/midi-Méditerranée - European Union (FEDER/ERDF) - Mecaprotec - ANRT |
| Statistics: | download |
| Deposited On: | 19 Oct 2020 07:30 |
Repository Staff Only: item control page