Ramenatte, Nicolas and Vernouillet, Annabelle and Mathieu, Stéphane and Vande Put, Aurélie
and Vilasi, Michel and Monceau, Daniel
A comparison of the high-temperature oxidation behaviour of conventional wrought and laser beam melted Inconel 625.
(2020)
Corrosion Science, 164. 108347. ISSN 0010-938X
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 4MB |
Official URL: https://doi.org/10.1016/j.corsci.2019.108347
Abstract
The microstructure and oxidation resistance of Laser Beam Melted (LBM) and Conventionally Manufactured (CM) Inconel 625 alloys were studied at 900 °C and 1050 °C. The microstructure of the LBM samples was cellular, with Nb and Mo segregations located at the cell walls. At 900 °C, the oxidation rate was similar for both materials but was clearly higher for the LBM material at 1050 °C. This high oxidation rate induced poor oxide scale compactness, void formation in the subsurface region and the formation of a high amount of Nb1.5Cr0.5O4 at the alloy-oxide interface.
Item Type: | Article |
---|---|
HAL Id: | hal-02972156 |
Audience (journal): | International peer-reviewed journal |
Uncontrolled Keywords: | |
Institution: | French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) Other partners > Université de Lorraine (FRANCE) |
Laboratory name: | |
Statistics: | download |
Deposited On: | 20 Oct 2020 08:49 |
Repository Staff Only: item control page