Metal dusting of Inconel 625 obtained by laser beam melting: Effect of manufacturing process and hot isostatic pressure treatment.
(2020)
Corrosion Science, 174. 108820. ISSN 0010-938X
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 16MB |
Official URL: https://doi.org/10.1016/J.CORSCI.2020.108820
Abstract
Metal dusting resistance of Inconel 625 alloy obtained by laser beam melting (LBM), compared to wrought alloy 625 was assessed during 9 500 h at 610 °C. Whatever the manufacturing process, the mass variations were very small when the systems were ground thanks to the formation of a uniform protective chromia layer. However, the high surface roughness was shown to be detrimental as the waviness favoured the local formation of an unprotective spinel oxide. Hot isostatic pressure (HIP) treatment recrystallized the alloy and increased its grain size. This reduced chromium diffusion towards the surface, explaining the poorer resistance of the LBM + HIP system.
Item Type: | Article |
---|---|
HAL Id: | hal-03033182 |
Audience (journal): | International peer-reviewed journal |
Uncontrolled Keywords: | |
Institution: | Other partners > Air Liquide (FRANCE) French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Université de Toulouse > Institut National des Sciences Appliquées de Toulouse - INSA (FRANCE) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) |
Laboratory name: | |
Statistics: | download |
Deposited On: | 09 Oct 2020 13:23 |
Repository Staff Only: item control page