Wang, Jianhua and Lu, Xiao-Gang and Sundman, Bo and Su, Xuping Thermodynamic reassessment of the Au–Te system. (2006) Journal of Alloys and Compounds, 407 (1 - 2). 106-111. ISSN 0925-8388
![[img]](https://oatao.univ-toulouse.fr/style/images/fileicons/application_pdf.png) |
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 367kB |
Official URL: http://dx.doi.org/10.1016/j.jallcom.2005.05.038
Abstract
The Au–Te binary system has been thermodynamically reassessed using the CALPHALD method. The excess Gibbs energy of the liquid phase was formulated with the Redlich–Kister expression and the AuTe2 intermetallic phase was treated as a stoichiometric compound. A set of self-consistent thermodynamic parameters for each phase has been obtained. Good agreement is reached between the calculated and experimental results. Additionally, the standard formation enthalpy and enthalpy of fusion of AuTe2 intermetallic phase have also been calculated.
| Item Type: | Article |
|---|---|
| Additional Information: | Thanks to Elsevier editor. The definitive version is available at http://www.sciencedirect.com The original PDF of the article can be found at Journal of Alloys and Compounds website : http://www.sciencedirect.com/science/journal/09258388 |
| Audience (journal): | International peer-reviewed journal |
| Uncontrolled Keywords: | |
| Institution: | Other partners > Xiangtan University - XTU (CHINA) Other partners > Royal Institute of Technology – KTH (SWEDEN) |
| Laboratory name: | School of Mechanical Engineering - SME (Xiangtan, China) - Institute of Materials Research Department of Materials Science and Engineering (Stockholm, Sweden) |
| Statistics: | download |
| Deposited On: | 18 Jun 2009 07:44 |
Repository Staff Only: item control page