Precipitation in original Duralumin A-U4G versus modern 2017A alloy

Abstract

Precipitation in Duralumin, a historic quaternary alloy of the type: Al–Cu–Mg–Si, was never fully studied nor observed by current electron microscopy techniques. This article presents the full characterization and comparison of two alloys: a Duralumin (A-U4G) from the 1950s collected on a vintage aircraft and its modern equivalent: a 2017A alloy. The as-received and peak-aging states were analysed with DSC, SAXS and TEM advanced techniques. It is shown that old Duralumin and modern 2017A present a similar nanoprecipitation in the as-received state and behave similarly upon artificial aging. As opposed to what has been reported in the past, three types of precipitates participating in hardening were found upon aging: θ’-Al2Cu, Q’(Q)-AlCuMgSi and Ω-Al2Cu.