Functionalisation of Ti6Al4V and hydroxyapatite surfaces with combined peptides based on KKLPDA and EEEEEEEE peptides

Rodriguez, Gabriela Melo and Bowen, James and Grossin, David and Ben-Nissan, Besim and Stamboulis, Artemis Functionalisation of Ti6Al4V and hydroxyapatite surfaces with combined peptides based on KKLPDA and EEEEEEEE peptides. (2017) Colloids and Surfaces B Biointerfaces, 160. 154-160. ISSN 0927-7765

(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader

Official URL: https://doi.org/10.1016/j.colsurfb.2017.09.022


Surface modifications are usually performed on titanium alloys to improve osteo-integration and surface bioactivity. Modifications such as alkaline and acid etching, or coating with bioactive materials such as hydroxyapatite, have previously been demonstrated. The aim of this work is to develop a peptide with combined titanium oxide and hydroxyapatite binders in order to achieve a biomimetic hydroxyapatite coating on titanium surfaces. The technology would also be applicable for the functionalisation of titanium and hydroxyapatite surfaces for selective protein adsorption, conjugation of antimicrobial peptides, and adsorption of specialised drugs for drug delivery. In this work, functionalisation of Ti6Al4V and hydroxyapatite surfaces was achieved using combined titanium-hydroxyapatite (Ti-Hap) peptides based on titanium peptide binder (KKLPDA) and hydroxyapatite peptide binder (EEEEEEEE). Homogeneous peptide coatings on Ti6Al4V surfaces were obtained after surface chemical treatments with a 30wt% aqueous solution of H2O2 for 24 and 48h. The treated titanium surfaces presented an average roughness of Sa=197nm (24h) and Sa=128nm (48h); an untreated mirror polished sample exhibited an Sa of 13nm. The advancing water contact angle of the titanium oxide layer after 1h of exposure to 30wt% aqueous solution of H2O2 was around 65°, decreasing gradually with time until it reached 35° after a 48h exposure, suggesting that the surface hydrophilicity increased over etching time. The presence of a lysine (L) amino acid in the sequence of the titanium binder resulted in fluorescence intensity roughly 16% higher compared with the arginine (R) amino acid analogue and therefore the lysine containing titanium peptide binder was used in this work. The Ti-Hap peptide KKLPDAEEEEEEEE (Ti-Hap1) was not adsorbed by the treated Ti6Al4V surfaces and therefore was modified. The modifications involved the inclusion of a glycine spacer between the binding terminals (Ti-Hap2) and the addition of a second titanium binder (KKLPDA) (Ti-Hap3 and Ti-Hap4). The combined Ti-Hap peptide which exhibited the strongest intensity after the titanium surface dip coating was KKLPDAKKLPDAEEEEEEEE (Ti-HAp4). On the other hand, hydroxyapatite surfaces, exhibiting an average roughness of Sa=1.42μm, showed a higher fluorescence for peptides with a higher negative net charge.

Item Type:Article
HAL Id:hal-02400322
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
Other partners > University of Technology, Sydney - UTS (AUSTRALIA)
Other partners > Walton Hall - The open University (UNITED KINGDOM)
Other partners > University of Birmingham (UNITED KINGDOM)
Laboratory name:
European Union’s Horizon 2020 research and innovation programme under the Marie Sklodowska-Curie
Deposited On:09 Dec 2019 13:30

Repository Staff Only: item control page