OATAO - Open Archive Toulouse Archive Ouverte Open Access Week

Effect of temperature on hydrogen embrittlement susceptibility of alloy 718 in Light Water Reactor environment

Galliano, Florian and Andrieu, Eric and Cloué, Jean-Marc and Odemer, Grégory and Blanc, Christine Effect of temperature on hydrogen embrittlement susceptibility of alloy 718 in Light Water Reactor environment. (2017) International Journal of Hydrogen Energy, 42 (33). 21371-21378. ISSN 0360-3199

[img]
Preview
(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
685kB

Official URL: https://doi.org/10.1016/j.ijhydene.2017.06.211

Abstract

A 718 superalloy, presenting a standard microstructure, was mechanically tested under uniaxial tensile loading at 80 °C and 300 °C in Light Water Reactor environment after an exposure at 300 °C for 200 h. Hydrogen embrittlement mechanism was clearly observed. In order to identify the most influent metallurgical parameters on hydrogen embrittlement, three “model” microstructures were synthesized to test the efficiency of carbides, δ, γ′ and γ” precipitates to trap hydrogen at different temperatures. Results showed that γ′ and γ” played the major role on the hydrogen embrittlement susceptibility of the alloy even though carbides and δ precipitates could also act as hydrogen traps and influence the final rupture mechanism. Results also characterized the influence of temperature on the fracture modes

Item Type:Article
HAL Id:hal-02404942
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
Other partners > MBDA (FRANCE)
Other partners > Spinodal Conseil (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
Laboratory name:
Statistics:download
Deposited On:11 Dec 2019 14:44

Repository Staff Only: item control page