Impedance study of the influence of chromates on the properties of waterborne coatings deposited on 2024 aluminium alloy

Abstract

Coatings formulated with either SrCrO4 or a mixture of Cr(VI)-free pigments were compared in an impedance study. In addition to classical EIS measurements carried out in the metal/coating/electrolyte configuration, the study involved measurement of the impedance of the coatings in the dry state, both before exposure to the electrolyte (0.5M NaCl solution) and after a 1-month exposure followed by a 12-month drying. The results were analysed with reference to models that assumed resistivity variations along the coating thickness. The resistivity-position dependence was close to a power law for dry coatings and close to exponential for wet coatings. In the latter, and for short immersion times, the exponential variation was located in the outer coating region, at shorter distances from the coating/solution interface, and then, for longer immersion times (>1 week), extended to the whole coating thickness. The effect of SrCrO4 leaching on the properties of the coating is discussed. For both coatings, the barrier effect remained high for a 1-month exposure.