Development of Representative Tests to Quantify the Susceptibility to Stress Corrosion Cracking of , '-Brass Used for Gas Transfer Devices

Berne, Clément and Andrieu, Eric and Reby, Jean and Sobrino, Jean-Michel and Blanc, Christine Development of Representative Tests to Quantify the Susceptibility to Stress Corrosion Cracking of , '-Brass Used for Gas Transfer Devices. (2015) ECS Transactions, 64 (27). 21-33. ISSN 1938-6737

[img]
Preview
(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
5MB

Official URL: https://doi.org/10.1149/06427.0021ecst

Abstract

Corrosion susceptibility of an α,β'-brass CuZn40Pb2 (CW617N), used for gas transfer devices, was investigated through accelerated corrosion tests at a constant anodic potential in NaNO3 solution with basic pHs. The anodic dissolution behavior of the α,β'-brass was characterized by a two stages-mechanism, with each stage including both dezincification and simultaneous dissolution phenomena of the β' phase but with different kinetics at each stage. Compressive or tensile stresses applied on brass specimens during the accelerated tests were observed largely to influence the anodic dissolution kinetics. Stresses were assumed to open or close the pores present in the dezincified β' phase, which promoted or slowed the dezincification mechanism, including with the Zn diffusion into the solution trapped inside of the pores.

Item Type:Article
HAL Id:hal-02475809
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:Other partners > Centre Technique des Industries Mécaniques - CETIM (FRANCE)
French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
Laboratory name:
Statistics:download
Deposited On:12 Feb 2020 11:00

Repository Staff Only: item control page