Benchikhi, Mohamed and El Ouatib, Rachida and Guillemet, Sophie
and Er-Rakho, Lahcen and Durand, Bernard
Structural and microstructural characterization of CuMo(1-x)WxO4 (x ≤ 0.12) ceramics sintered by spark plasma sintering.
(2015)
GlobalJournal of EngineeringScience andResearchManagement, 2 (12). 123-128. ISSN 2349-4506
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 471kB |
Official URL: http://www.gjesrm.com/Issues%20PDF/Archive-2015/December-2015/15.pdf
Abstract
Cupric molybdate CuMoO4is an interesting material due to their rich electrical, optical and magnetic properties. In this work, Solid solutions CuMo(1-x)WxO4(x≤0.12) were obtained by pyrolysis at 400 -700°C for 2 hours of a polymeric precursors elaborated by polymerizable complex method. For x ≤ 0.075, they were isostructural with α-CuMoO4 and for 0.075<x≤0.12, they were isostructural with γ-CuMoO4. Spark Plasma Sintering (SPS) at 300°C for 5 min under an applied pressure of 200 MPa led to variety CuMoO4-III for tungsten contents in the range 0.075-0.12.
Item Type: | Article |
---|---|
HAL Id: | hal-02094693 |
Audience (journal): | International peer-reviewed journal |
Uncontrolled Keywords: | |
Institution: | French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Other partners > Université Hassan II Casablanca - UH2C (MOROCCO) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) |
Laboratory name: | |
Statistics: | download |
Deposited On: | 09 Apr 2019 17:01 |
Repository Staff Only: item control page