Influence of DE-value on the physicochemical properties of maltodextrin for melt extrusion processes

Castro Gutierrez, Natalia and Durrieu, Vanessa and Raynaud, Christine and Rouilly, Antoine Influence of DE-value on the physicochemical properties of maltodextrin for melt extrusion processes. (2016) Carbohydrate Polymers, 144. 464-473. ISSN 0144-8617

[img]
Preview
(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
299kB

Official URL: https://doi.org/10.1016/j.carbpol.2016.03.004

Abstract

In this study, five different types of maltodextrins (DE-2, DE-6, DE-12, DE-17 and DE-19) were characterized for the physico-chemical properties. TGA, DVS and SEC analyses were carried out and additionally apparent melt-viscosity (in a micro-extruder) and the glass transition temperature (analyzed by DMA) of maltodextrin/plasticizer mixtures were also measured in order to evaluate both the effect of plasticizer nature and content and the effect of the DE-value. For this, three plasticizing agents were compared: water, d-sorbitol and glycerin. The adsorption isotherms showed that depending on the DE-value and the relative humidity they were exposed to, different behavior could be obtained. For example, for relative humidities below 60% RH maltodextrin DE-2 was the least hygroscopic. And on the contrary for relative humidities above 75% RH maltodextrin DE-2 was the most hygroscopic. The rheology measurements showed that the viscosity decreased with the increase of the DE-value and with the plasticizer content, as expected. On the contrary, no direct correlation could be established between the DE-value and the glass transition temperature. These results demonstrated that to predict maltodextrins behavior and to better adapt the process conditions, combined analyses are mandatory as the DE-value alone is not sufficient. The most compelling evidence was obtained by size exclusion chromatography, which pointed out that maltodextrins had a bimodal molecular weight distribution composed of high and low molecular weight oligo-saccharides. Indeed, maltodextrins are highly polydisperse materials (i.e. polydispersity index ranging from 5 to 12) and that should be the reason why such distinct behaviors were observed in some of the physico-chemical analyses that were preformed.

Item Type:Article
HAL Id:hal-02083687
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
French research institutions > Institut National de la Recherche Agronomique - INRA (FRANCE)
Laboratory name:
Statistics:download
Deposited On:29 Mar 2019 09:51

Repository Staff Only: item control page