Influence of the microstructure on the corrosion behaviour of 2024 aluminium alloy coated with a trivalent chromium conversion layer.
(2018)
Corrosion Science, 142. 119-132. ISSN 0010-938X
|
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader 685kB |
Official URL: https://doi.org/10.1016/j.corsci.2018.07.007
Abstract
The influence of 2024 aluminium alloy microstructure on the protective properties of trivalent chromium process (TCP) coatings was studied: samples aged at 190 °C were analysed by comparison to a T3 state. The surface Cu coverage after deoxidation was higher for long-aged samples because nanometer scale Cu-rich precipitates formed during ageing behaved as distinct electrochemical entities and contributed to the formation of copper deposits. The growth mechanisms and kinetics of TCP coatings were directly related to the surface Cu coverage: thicker but more defective TCP coatings formed on long-aged samples leading to the lowest anti-corrosion properties.
| Item Type: | Article |
|---|---|
| HAL Id: | hal-01989678 |
| Audience (journal): | International peer-reviewed journal |
| Uncontrolled Keywords: | |
| Institution: | French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE) Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE) Other partners > MÉCAPROTEC Industries (FRANCE) Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE) |
| Laboratory name: | |
| Statistics: | download |
| Deposited On: | 22 Jan 2019 14:01 |
Repository Staff Only: item control page