Elaboration, microstructure and reactivity of Cr3C2 powders of different morphology

Loubière, Sophie and Laurent, Christophe and Bonino, Jean-Pierre and Rousset, Abel Elaboration, microstructure and reactivity of Cr3C2 powders of different morphology. (1995) Materials Research Bulletin, 30 (12). 1535-1546. ISSN 0025-5408

[img]
Preview
(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
490kB

Official URL: http://dx.doi.org/10.1016/0025-5408(95)00123-9

Abstract

Cr,C, powders have been prepared by heat-treatment of metastable chromium oxides of controlled morphology in H2-CH4 atmosphere. Starting with these highly reactive oxides allows formation of Cr,C, at 700°C. The reaction is pseudomorphic and d&rent grain shapes (needles, rods, spheres and polyhedra) have been obtained. The size distribution is narrow and the grain size is generally of the order of a few tens of micrometers, but the "spheres" are in fact made up of aggregates of small platelets about 1.5 pm wide and 0.7 pm thick. The oxidation in air of the carbides was studied by thermal analyses (TGA, DTG and DSC) and was found to proceed in four steps in the 250-700°C range. The differences observed between the carbides are related to their morphology and texture.

Item Type:Article
Additional Information:Thanks to Elsevier editor. The definitive version is available at http://www.sciencedirect.com The original PDF of the article can be found at Materials Research Bulletin website : http://www.sciencedirect.com/science/article/pii/0025540895001239#
HAL Id:hal-00966897
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UT3 (FRANCE)
Laboratory name:
Statistics:download
Deposited On:27 Mar 2014 14:27

Repository Staff Only: item control page