Effect of temperature on high pressure cellulose compression

Vaca Medina, Guadalupe and Jallabert, Bastien and Viet, David and Peydecastaing, Jérôme and Rouilly, Antoine Effect of temperature on high pressure cellulose compression. (2013) Cellulose, 20 (5). 2311-2319. ISSN 0969-0239

[img]
Preview
(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
6MB

Official URL: http://dx.doi.org/10.1007/s10570-013-9999-y

Abstract

The effect of temperature during cellulose compression has been studied using mechanical testing, particle size analysis, density and Pressure-Volume-Temperature (PVT) measurements, crystallinity index, SEM photographs and water sorption isotherms. Commercial cellulose powder samples with different crystallinity levels were compacted at high pressure (177 MPa) for 10 minutes at two different temperatures: 25 and 160 °C. 3 point bending test results for compressed samples are discussed. When pressure was applied directly to powders at room temperature, the cellulose sample with the highest level of crystallinity showed an increase in its crystallinity index of about 5 %, while this was about 22 % for the sample with the lowest level. These increases were even higher at 160 °C attaining 8 and 33 % respectively. Using density measurements, a densification phase related to this crystallinization was observed, and the PVT diagrams from different cellulose samples showed that this was associated with high temperatures. Water sorption isotherms were made on cellulose samples before and after compression. They showed a diminution of cellulose sorption capacity after compression at 160 °C, revealing the effect of temperature on high-pressure cellulose compression, reducing specific surface area. Events of this nature suggest a sintering mechanism, when temperature is associated with high pressure during cellulose compression.

Item Type:Article
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:Université de Toulouse > Institut National Polytechnique de Toulouse - Toulouse INP (FRANCE)
French research institutions > Institut National de la Recherche Agronomique - INRA (FRANCE)
Other partners > The Green Factory (FRANCE)
Laboratory name:
Laboratoire de Chimie Agro-Industrielle - LCA (Toulouse, France) - Fractionnement et transformation des agroressources
Statistics:download
Deposited On:22 Nov 2013 10:59

Repository Staff Only: item control page