Dip-coated La2Ti2O7 as a buffer layer for growth of Bi3.25La0.75Ti3O12 films with enhanced (0 1 1) orientation

Abstract

Thin-films of La2Ti2O7 were obtained by dip-coating process using a precursor salt in nitric acid solution. The effects of solution concentration, withdrawal speed, post-annealing duration and temperature were investigated both on grain size and orientation of the La2Ti2O7 thin layers. In addition, a target with the required stoichiometry for PVD deposition of La-substituted Bi4Ti3O12 (BLT) was successfully sintered by spark plasma sintering (SPS) at 750 ◦C. Finally (0 1 1)-oriented BLT ferroelectric films have been grown by RF sputtering on (1 1 0)-oriented La2Ti2O7 polycrystalline thin-film. A preferential orientation of BLT thin films has been obtained after annealing at a temperature lower than 650 ◦C.