Malfatti, C.F and Veit, H.M. and Santos, C.B and Metzner, M. and Hololeczek, H. and Bonino, Jean-Pierre Heat Treated NiP–SiC Composite Coatings: Elaboration and Tribocorrosion Behaviour in NaCl Solution. (2009) Tribology Letters, vol. 36 (n° 2). pp. 165-173. ISSN 1573-2711
(Document in English)
PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
Official URL: http://dx.doi.org/10.1007/s11249-009-9471-1
Tribocorrosion behaviour of heat-treated NiP and NiP–SiC composite coatings was investigated in a 0.6 M NaCl solution. The tribocorrosion tests were performed in a linear sliding tribometer with an electrochemical cell interface. It was analyzed the influence of SiC particles dispersion in the NiP matrix on current density developed, on coefficient of friction and on wear volume loss. The results showed that NiP–SiC composite coatings had a lower wear volume loss compared to NiP coatings. However, the incorporation of SiC particles into the metallic matrix affects the current density developed by the system during the tribocorrosion test. It was verified that not only the volume of co-deposited particles (SiC vol.%) but also the number of SiC particles per coating area unit (and consequently the SiC particles size) have made influence on the tribocorrosion behaviour of NiP–SiC composite coatings.
|Additional Information:||Thanks to Springer Netherlands editor. The definitive version is available at http://www.springerlink.com/ The original PDF of the article can be found at Tribology Letters website : http://www.springerlink.com/content/70mp234n7g474r8j/|
|Audience (journal):||International peer-reviewed journal|
|Institution:|| Université de Toulouse > Institut National Polytechnique de Toulouse - INPT|
Université de Toulouse > Université Paul Sabatier-Toulouse III - UPS
?? fraunhofer_inst_ipa_DE ??
French research institutions > Centre National de la Recherche Scientifique - CNRS
Other partners > Universidade Federal do Rio Grande do Sul - UFRGS (BRAZIL)
|Deposited By:||Nihad Lahdifi|
Repository Staff Only: item control page