Influence of the ageing conditions and the initial microstructure on the precipitation of α phase in Ti-17 alloy

Maury, Nicolas and Denand, Benoît and Dehmas, Moukrane and Archambeau-Mirguet, Claude and Delfosse, Jérôme and Aeby-Gautier, Elisabeth Influence of the ageing conditions and the initial microstructure on the precipitation of α phase in Ti-17 alloy. (2018) Journal of Alloys and Compounds, 763. 446-458. ISSN 0925-8388

[img]
Preview
(Document in English)

PDF (Author's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
2MB

Official URL: https://doi.org/10.1016/j.jallcom.2018.04.302

Abstract

The precipitation of α phase during ageing was investigated in the near-β titanium alloy Ti-17 considering either a fully βmetastable initial microstructure or a 35% αprimary + 65% βmetastable initial microstructure. In-situ electrical resistivity and high energy X-ray diffraction measurements revealed the influence of the initial microstructure, with different α morphologies (size and distribution of αprimary), as well as the heating rate on the precipitation sequences and kinetics following the decomposition of the β-metastable phase. Various amounts of metastable phases (ωisothermal and α″isothermal) precipitate in temperature ranges that increase with the heating rate. From temperatures about 500 °C, the orthorhombic α″isothermal structure evolved towards the hexagonal close-packed α as temperature increased. SEM microstructure characterisations showed that slow heating rates promoted a fine and dense α precipitate distribution through the formation of ωisothermal and/or α″isothermal, leading to higher hardness values. A higher heating rate restricted the precipitation of α″isothermal and shifted to the one of α at a higher temperature, leading to coarser precipitates. Furthermore, precipitation kinetics of α″isothermal/α were quicker considering an initial intragranular α precipitation as compared to α colonies.

Item Type:Article
HAL Id:hal-01985586
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:Other partners > Airbus (FRANCE)
French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Institut National Polytechnique de Toulouse - INPT (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UPS (FRANCE)
Other partners > Université de Lorraine (FRANCE)
Laboratory name:
Statistics:download
Deposited By: cirimat webmestre
Deposited On:18 Jan 2019 09:30

Repository Staff Only: item control page