Heterojunction p-Cu2O/ZnO-n solar cell fabricated by spark plasma sintering

Tenailleau, Christophe and Salek, Guillaume and Le, Thi Ly and Duployer, Benjamin and Demai, Jean-Jacques and Dufour, Pascal and Guillemet-Fritsch, Sophie Heterojunction p-Cu2O/ZnO-n solar cell fabricated by spark plasma sintering. (2017) Materials for Renewable and Sustainable Energy, 6 (18). 1-7. ISSN 2194-1459

[img]
Preview
(Document in English)

PDF (Publisher's version) - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
1MB

Official URL: http://dx.doi.org/10.1007/s40243-017-0102-8

Abstract

Cuprous oxide and zinc oxide nanoparticles were prepared at room temperature by inorganic polycondensation. X-ray diffraction (XRD) analyses show that the oxide phases formed are pure and well crystallized. The spark plasma sintering (SPS) technique was successfully used to prepare dense nanoceramics with superimposed layers of Cu2O and ZnO nanopowders. Sintering conditions were optimized to densify the ceramics without phase transformation or diffusion. These ceramics were also characterized by XRD and scanning electron microscopy (SEM), as well as X-ray computed tomography (XCT). SEM and XCT showed that nanograins are preserved after SPS throughout both oxide materials, while a smaller layer (*20 lm) of pure oxide phase with larger grains is formed in between Cu2O and ZnO during the sintering process. The SPS technique results in high material density, with the absence of porosity and cracks, homogenous distribution, and a good phase separation. This is the first time that such as-prepared dense oxide-based heterojunction exhibits a photovoltaic effect under illumination opening a new route for preparing solar cells.

Item Type:Article
Additional Information:Thanks to Springer editor. The original PDF of the article can be found at https://link.springer.com/article/10.1007%2Fs40243-017-0102-8
HAL Id:hal-01754855
Audience (journal):International peer-reviewed journal
Uncontrolled Keywords:
Institution:French research institutions > Centre National de la Recherche Scientifique - CNRS (FRANCE)
Université de Toulouse > Institut National Polytechnique de Toulouse - INPT (FRANCE)
Université de Toulouse > Université Toulouse III - Paul Sabatier - UPS (FRANCE)
Laboratory name:
Statistics:download
Deposited By: cirimat webmestre
Deposited On:30 Mar 2018 09:14

Repository Staff Only: item control page